Fabrication of novel silicon carbide-based nanomaterials with unique hydrophobicity and microwave absorption property

Novel SiC-based nanomaterials, namely the nitrogen and aluminum co-doped SiC@SiO₂ core-shell nanowires and nitrogen-doped SiO₂/Al₂O₃ nanoparticles, have been fabricated through a facile thermal treatment process based on the chemical vapor deposition and vapor-liquid reaction. These nanomaterials show remarkable hydrophobicity with a water contact angle (CA) over 140°, which are aroused by the surface zigzag morphology of the nanostructures and the hydrocarbyl groups generated during the preparation process. Moreover the nanocomposites also exhibit relatively prominent microwave absorption (MA) properties in the frequency range of 2.0-18.0 GHz. The minimum reflection loss (RL) value as low as −23.68 dB can be observed at 14.16 GHz when the absorber thickness is 2.6 mm with a loading rate of 16.7 wt%. And the nanocomposites-based absorbent can achieve an effective absorption bandwidth (RL < −10 dB) of 4.48 GHz with the absorbent thickness of 2.5 mm. This enhanced microwave attenuation performance can be attributed to multiple polarizations and perfect impedance matching conditions, as well as multiple internal reflections. These marvelous properties make these N and Al co-doped SiC@SiO₂ core-shell nanowires and N-doped SiO₂/Al₂O₃ nanoparticles display extensive application potential as MA materials in harsh environment.     

伞帽用高铬铸铁在热强碱腐蚀环境下的磨损分析

针对氧化铝行业中常用的Cr28和Cr20高铬铸铁伞帽在相同工况条件下的磨损机理进行分析,并对比研究了实际生产中两种失效材料的成分、组织及性能。结果表明,伞帽部件在高温强碱腐蚀条件下受到外界冲刷时,磨损量由微切削磨损与变形磨损这两种机制共同决定。含铬量较高的Cr28高铬铸铁,其冲刷和抗腐蚀磨损性能均优于Cr20高铬铸铁。伞帽服役寿命主要受浆料和表层的铸铁材料两大因素影响。两种试验材料经淬火+回火处理后,基体组织中主要为回火马氏体+M₇C₃型碳化物+少量残留奥氏体,其中含铬量较高的Cr28高铬铸铁中共晶碳化物含量更高,且分布更加弥散,其平均硬度值为64.0 HRC,高于Cr20高铬铸铁的60.2 HRC。最终确定Cr28高铬铸铁作为伞帽材质更能满足氧化铝生产及设备检修周期的需要。     

Ferroelastic domain structure and phase transition in single-crystalline [PbZn1/3Nb2/3O3]1-x[PbTiO3]x observed via in situ x-ray microbeam

(1-x)Pb(Zn_1/3Nb_2/3)O₃-xPbTiO₃ ((1-x)PZN-xPT in short) is one of the most important piezoelectric materials. In this work, we extensively investigated (1-x)PZN-xPT (x = 0.07–0.11) ferroelectric single crystals using in-situ synchrotron μXRD, complemented by TEM and PFM, to correlate microstructures with phase transitions. The results reveal that (i) at 25 °C, the equilibrium state of (1-x)PZN-xPT is a metastable orthorhombic phase for x = 0.07 and 0.08, while it shows coexistence of orthorhombic and tetragonal phases for x = 0.09 and x = 0.11, with all ferroelectric phases accompanied by ferroelastic domains; (ii) upon heating, the phase transformation in x = 0.07 is Orthorhombic → Monoclinic → Tetragonal → Cubic. The coexistence of ferroelectric tetragonal and paraelectric cubic phases was in-situ observed in x = 0.08 above Curie temperature (T_C), and (iii) phase transition can be explained by the evolution of the ferroelectric and ferroelastic domains. These results disclose that (1-x)PZN-xPT are in an unstable regime, which is possible factor for its anomalous dielectric response and high piezoelectric coefficient.     

DZZ5型自动气象站多媒体故障排查系统的设计与研发

为更有针对性地进行故障排除工作,文章设计研发了一款多媒体软件平台,嵌入细化后的DZZ5型自动气象站各观测要素的故障排查流程,并在相应故障检测节点中添加文字、图片和操作视频。用户可按照流程逐一进行排查操作,或者搜索关键字查看节点内容。同时提供带有关键字查询功能的故障实例库,供基层装备保障业务人员参考。     

Microstructure and damage evolution of SiCf/PyC/SiC and SiCf/BN/SiC mini-composites: A synchrotron X-ray computed microtomography study

SiC_f/PyC/SiC and SiC_f/BN/SiC mini-composites comprising single tow SiC fibre-reinforced SiC with chemical vapor deposited PyC or BN interface layers are fabricated. The microstructure evolutions of the mini-composite samples as the oxidation temperature increases (oxidation at 1000, 1200, 1400, and 1600?°C in air for 2?h) are observed by scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction characterization methods. The damage evolution for each component of the as-fabricated SiC_f/SiC composites (SiC fibre, PyC/BN interface, SiC matrix, and mesophase) is mapped as a three-dimensional (3D) image and quantified with X-ray computed tomography. The mechanical performance of the composites is investigated via tensile tests.The results reveal that tensile failure occurs after the delamination and fibre pull-out in the SiC_f/PyC/SiC composites due to the volatilization of the PyC interface at high temperatures in the air environment. Meanwhile, the gaps between the fibres and matrix lead to rapid oxidation and crack propagation from the SiC matrix to SiC fibre, resulting in the failure of the SiC_f/PyC/SiC composites as the oxidation temperature increases to 1600?°C. On the other hand, the oxidation products of B₂O₃ molten compounds (reacted from the BN interface) fill up the fracture, cracks, and voids in the SiC matrix, providing excellent strength retention at elevated oxidation temperatures. Moreover, under the protection of B₂O₃, the SiC_f/BN/SiC mini-composites show a nearly intact microstructure of the SiC fibre, a low void growth rate from the matrix to fibre, and inhibition of new void formation and the SiO₂ grain growth from room to high temperatures. This work provides guidance for predicting the service life of SiC_f/PyC/SiC and SiC_f/BN/SiC composite materials, and is fundamental for establishing multiscale damage models on a local scale.     

Large increase of Curie temperature in (110)-oriented La0.7Sr0.3MnO3 films

From the perspectives of scientific researches and practical applications, it is desirable to explore high operating temperature ferromagnetic films. The effect of biaxial strain on magnetic properties of (110)-oriented La_0.7Sr_0.3MnO₃ films was studied. High quality La_0.7Sr_0.3MnO₃ films were grown on (110)-oriented perovskite single crystal substrates using pulsed laser deposition, varying substrate-induced misfit strains from ??2.27–0.75%. A remarkable enhancement of Curie temperature has been achieved for (110)-oriented La_0.7Sr_0.3MnO₃ films clamped with small misfit strains (i.e., grown on LAST (110)). The enhanced Curie temperature of (110)-oriented La_0.7Sr_0.3MnO₃ films could be attributed to the misfit strain between the films and the underlying substrates and may have technological implication for applications at high temperature environments.     

Preparation of ZrC/SiC porous self-supporting monoliths via sol-gel process using polyethylene glycol as phase separation inducer

We present a straightforward method via sol-gel process using polyethylene glycol (PEG) as phase separation inducer to prepare zirconium carbide/silicon carbide (ZrC/SiC) porous monoliths. Organic/inorganic hybrid gels are prepared using zirconium oxychloride, furfuryl alcohol, and tetraethyl orthosilicate as major starting materials. In the presence of PEG, crack-free hybrid monoliths are obtained by drying the wet gels under ambient pressure, whereas in the absence of PEG, the wet gels break into pieces as expected. PEG plays a key role in maintaining the macroscopic shape of the monoliths. After ceramization at 1300–1500?°C, ZrC/SiC porous monoliths are obtained. SEM and mercury intrusion porosimetry data show that PEG also has strong influence on the microstructures of the monoliths. The compressive strengths of the ceramic monoliths are in the range of 0.3 to 0.7?MPa. And their compressive behavior starts to differ due to the changes in their microstructures, especially the pore structure.